Method for preparing a highly active, unsupported high surface-area MoS2 catalyst

ABSTRACT

The present invention is a new and simple method of decomposing ammonium tetrathiomolybdate (ATTM) in an organic solvent with added water under H 2  pressure. Model compound reactions of 4-(1-naphthylmethyl)bibenzyl (NMBB) were carried out at 350-425° C. under H 2  pressure in order to examine the activity of the Mo sulfide catalysts generated from ATTM with and without added water for C—C bond cleavage and hydrogenation of aromatic ring. The Mo sulfide catalysts generated from ATTM with added water were much more effective for C—C bond cleavage and hydrogenation of aromatic moieties at 350-425° C. than those from ATTM alone. Two-step tests revealed that the addition of water is effective for generating highly active Mo sulfide catalyst from ATTM, but water itself does not promote catalytic conversion. Removal of water after the decomposition of ATTM with added water at 350-400° C. under H 2  pressure by hot purging gives highly active Mo sulfide catalyst.

This application is a Continuation-In-Part application of U.S. patent application Ser. No. 09/413,121 filed Oct. 6, 1999 now U.S. Pat. No. 6,156,693.

BACKGROUND

Various catalysts have been tested for conversion and upgrading of liquid and solid fuels. Among them molybdenum sulfide-based catalysts are widely used for hydroprocessing and hydrodesulfurization. Mo sulfide can be prepared from molybdate or thiomolybdate. A well-established method for preparing MoS₂ catalyst involves decomposition of ammonium tetrathiomolybdate (ATTM) in an inert gas or in H₂. The MoS₂ catalyst generated from decomposition of ATTM is more active than that from sulfidation of molybdenum oxide or the reagent MOS₂, and thus ATTM has been used as catalyst precursor for generation of active. The surface area values for thus-prepared MoS₂ catalysts are relatively low. Usually somewhere between 6-70 m²/g. It is desirable to have a MoS₂ catalysts with higher surface area values than currently available. It is also desirable to have a MoS₂ catalysts that is more active than currently available.

SUMMARY OF THE INVENTION

The present invention is a new and simple method of decomposing ammonium tetrathiomolybdate (ATTM) in an organic solvent with added water under H₂ pressure. Model compound reactions of 4-(1-naphthylmethyl)bibenzyl (NMBB) were carried out at 350-425° C. under H2 pressure in order to examine the activity of the Mo sulfide catalysts generated from ATTM with and without added water for C—C bond cleavage and hydrogenation of aromatic ring. The Mo sulfide catalysts generated from ATTM with added water were much more effective for C—C bond cleavage and hydrogenation of aromatic moieties at 350-425° C. than those from ATTM alone. Two-step tests revealed that the addition of water is effective for generating highly active Mo sulfide catalyst from ATTM, but water itself does not promote catalytic conversion. Removal of water after the decomposition of ATTM with added water at 350-400° C. under H₂ pressure by hot purging gives highly active Mo sulfide catalyst.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a table of the results from a BET Surface Area of the catalysts prepared from ATTM at 350-400° C.;

FIG. 2 is a SEM of Mo sulfide prepared at 375° C. from ATTM alone (left) and from ATTM with added water (right) at 375° C.;

FIG. 3 is a XRD of Mo sulfide prepared at 375° C. from ATTM+H₂O (top), ATTM alone (middle) and Aldrich MoS2 reagent (bottom);

FIG. 4 is a XPS survey spectra of Mo sulfide prepared at 375° C. from ATTM alone (top), ATTM+H₂O(middle) and Aldrich MoS2 reagent (bottom);

FIG. 5 is a XPS Mo 3d spectra of Mo sulfide prepared at 375° C. from ATTM alone (top), ATTM+H₂O(middle) and Aldrich MoS, reagent (bottom);

FIG. 6 is a XPS S 2p spectra of Mo sulfide prepared at 375° C. from ATTM alone (top), ATTM+H₂O(middle) and Aldrich MoS, reagent (bottom);

FIG. 7 is a table of the results surface area and pore volume of fresh catalysts pepared from ATTM at 375° C.;

FIG. 8 is a structure of 4-(1-naphthylmethyl)bibenzyl (NMBB) and its potential cleavage sites;

FIG. 9 is a table of the results of noncatalytic hydrogenolysis of NMBB in 1.48 g tridecane under 6.9 MPa hydrogen;

FIG. 10 is a table of the results of effect of Mo catalyst precursor on hydrogenolysis of NMBB in 1.48 g tridecane under 6.9 MPa hydrogen;

FIG. 11 is a table of the results of effect of Mo catalyst precursor on hydrogenolysis of NMBB in 2.95 g tridecane under 6.9 MPa hydrogen;

FIG. 12 is a comparison of catalytic activity of Mo sulfide in situ generated from ATTM (left) and ATTM+H₂O for NMBB conversion in about 3 g n-tridecane solvent at 350° C.;

FIG. 13 is a comparison of catalytic activity of Mo sulfide in situ generated from ATTM (left) and ATTM+H₂O for NMBB conversion in about 1.5 g n-tridecane solvent at 350° C.; and

FIG. 14 is a table of conversion of NMBB in two-step tests using ATTM+H₂O as catalyst precursor in the first step.

DETAILED DESCRIPTION

The present invention provides a new and simple method to prepare a high-surface-area unsupported MoS₂ type catalysts by decomposing ATTM in an organic solvent in the presence of added water under hydrogen pressure.

The dispersed (unsupported) MoS catalyst particles are prepared by decomposing ATTM in normal tridecane solvent in the presence of added water under hydrogen pressure at 350, 375 and 400° C. in a micro autoclave. Characterization of the catalysts were performed using various techniques, including BET (first conducted on Micromeritics Gemini 2375, later on Quantachrome Autosorb-1), SEM (conducted on Philips XL-20), XRD (Philips Automated Powder Diffractomer, Cu Ka), XPS (Mg Ka, 14 keV at 20 mA, on Kratos Analytical XSAM800 PCI), TPO (on Mettler TG50, from r.t. to 600° C. in an air flow).

The BET analysis is shown in FIG. 1, which indicates that the Mo sulfide samples produced from ATTM+H₂O at 350-400° C. have much higher surface area (286-335 m²/g) than those (54-70 m²/g from ATTM alone (the word “alone” here means without the addition of water). For example. the surface area of the Mo sulfide prepared at 375° C. from ATTM+H₂O is 342 m²/g, which is about times that of the sample from ATTM without water (70 m²/g).

SEM photos of the Mo sulfide samples prepared at 375° C. are shown in FIG. 2. It is clear from SEM examination that the samples produced from ATTM+H₂O at 350-400° C. are much more porous and their surfaces are rough. On the other hand, Mo sulfides from ATTM alone at 350-400° C. they have a crystalline morphology, and have flat and smooth surface with visible cracks.

XRD profiles in FIG. 3 indicate that. compared to reagent MoS₂, the MoS₂ from ATTM are poorly crystalline. The XRD patterns of the MoS₂ from ATTM at 350-400° C. are very similar to those reported in the industry for MoS₂, From comparative examination, it becomes clear that the samples prepared from ATTM alone and those from ATTM+H₂O have similar XRD patterns in general, suggesting that the sample from ATTM+H₂O is MoS₂ like material. However, the 002 peak of the latter (from ATTM+H₂O) is broader and has a much lower intensity. This trend was observed for all the samples prepared at 350° C., 375° C. and 400° C. The very weak 002 peak suggests that the degree of MoS₂ layer stacking is much smaller in the samples prepared from ATTM+H₂O than in the samples from ATTM alone. On the other hand, it is known that XRD is not sensitive to surface species, and it can not detect the extremely small particles below <30 A. Therefore, we also examined the surface of the Mo sulfide catalysts by X-ray photoelectroscopy (XPS).

The XPS spectra of the samples were measured in two modes: a survey scan for examining the overall composition (FIG. 4), and high resolution scans for the Mo_(3d) (FIG. 5), S_(2p) (FIG. 6), S_(2s), C_(1s) and O_(1s) peaks. The survey spectra (FIG. 4) show that they are similar materials consisting of Mo and S. However, the commercial reagent MoS₂ from Aldrich and the sample from ATTM alone also show the C_(1s) peak at 284.6 eV. The MoS₂ reagent contains significantly more carbon than all the other samples. We also conducted an acetane washing and vacuum-drying of Aldrich MoS reagent followed by its XPS analysis; since the samples from ATTM with or without added water were washed with acetone. The acetone washing reduced the C_(1s) peak intensity for MoS₂ reagent but it is still much higher than that of MoS₂ from ATTM alone. However, the C_(1s) peak of the sample from ATTM+H₂O is very small and close to baseline/noise level. It is also interesting to note that O_(1s) peak can also be seen around 530 eV from the spectra for Aldrich MoS₂ reagent and that from ATTM, but the O_(1s) peak for the sample from ATTM+H₂O is the smallest among the 3 types of samples, despite the use of water during sample preparation.

Temperature-programmed oxidation (TPO) of the samples in an air flow (conducted using TGA) revealed that the Mo sulfide from ATTM+H₂O can be oxidized at lower temperature and at faster speed. In doing repeated sample analysis, we also observed that once exposed to air, the Mo sulfide samples can lose its surface area partially after storage for weeks, and for these samples the peak for TPO shifts to a higher temperature. This change was more pronounced with the sample prepared from ATTM+H₂O. Subsequently, we stored the catalyst samples in n-tridecane solvent and only dried it immediately before use. The surface area value for such freshly prepared catalyst from ATTM+H₂O at 375° C. (as shown in FIG. 7) is considerably higher than that shown in FIG. 1, which was measured after the sample was exposed to air and stored in the closed Pyrex vial for several days.

4(1-naphthylmethyl)bibenzyl, abbreviated as NMBB has been used as a model compound for examining activity and selectivity of various catalysts, since there are different types of potential cleavage sites of C—C bonds and both monocyclic and bicyclic aromatic moieties in the compound, as illustrated in FIG. 8. Model compound reactions of NMBB were carried out at 350-425° C. under H₂ pressure in order to examine the activity of the Mo sulfide catalysts generated from ATTM with and without added water for C—C bond cleavage and hydrogenation of aromatic ring. ATTM and n-tridecane solvent were purchased from Aldrich, and NMBB was purchased from TCI America. ATTM and NMBB were used without further purification. In this work, a bottle of newly purchased ATTM was used in all experiments on NMBB runs, and the reagent bottle was stored in a refrigerator in order to minimize oxidative degradation.

Testing to compare preparation of the Mo sulfide catalysts generated from ATTM with and without added water were done with a one-step test and a two-step test. For both tests a horizontal tubing microautoclave reactor with a capacity of 25 mL was loaded with ca. 0.8 mmol (0.258 g) of NMBB, 1 wt % catalyst precursor ATTM (1 wt % Mo based on NMBB) and 1.47 g or 2.95 g of solvent (n-tridecane). ATTM was added to the reactor in its powder form (as in the fresh reagent vial from Aldrich). When water was added, the weight ratio of H₂O to NMBB was kept at 0.56. The amount of water and the amount of NMBB were determined based on prior work in catalytic coal conversion and model compound studies using NMBB. The sealed reactor was purged four times with H₂ and then pressurized with 6.9 MPa H₂ at room temperature for all experiments. A preheated fluidized sand bath was used as the heating source, and the reactor was vertically agitated to provide mixing (about 240 strokes/min). After the reaction, the microautoclave was quenched in a cold water bath. The contents were washed out with 20-30 mL acetone, and filtered through a low speed filter paper for subsequent GC analysis of the filtrate. In addition for the two-step test, the active Mo sulfide catalyst was prepared using ATTM in the presence of n-tridecane solvent with added H₂O under H₂ pressure without NNIBB in the 25-mL microautoclave. Then the water vapor and H₂S and NH₃ gases generated from ATTM decomposition were removed from the reactor by hot venting at 200° C. for 35 min. Subsequently the reactor was opened and NMBB was added into the reactor and then the reaction was conducted at 350° C. in a similar manner as described above.

The products from both tests were identified by GC-MS using a Hewlet-Packard 5890 II GC coupled with a HP 5971 A mass-selective detector operating at electron impact mode (EI, 70 eV). The column used for GC-MS was a J&W DB-17 column; 30-m×0.25-mm, coated with 50% phenyl-50% methylpolysiloxane with a coating film thickness of 0.25 mm. For quantification, a Perkin Elmer 8500 GC flame ionization detector and the same type of DB-17 column were used. Both GC and GC-MS were programmed from 40 to 280° C. at a heating ratio of 6° C./min, with a initial holding time of 5 min and a final holding time of 18 min. The GC response factors for NMBB and 7 of the products were determined using pure compounds. The NMBB conversion is defined as {[NMBB (wt) charged−NMBB (wt) recovered]/NMBB (wt) charged]}×100, and the molar yields of products are defined as [product (mol)/NMBB (mol) charged]×100. Since the products mainly include the compounds from both C—C bond cleavage and partial hydrogenation of NMBB, the sums of product yields are generally less than twice the value of the conversion.

FIGS. 9 and 10 show the results of noncatalytic and catalytic runs of NMBB, respectively, at 350, 375, 400, 425 and 450° C. using a small amount of n-TRIDECANE solvent (1.48 g). Without ATTM, the conversions of NMBB were negligible at 350-375° C., low but observable at 400-425° C. Only when temperature is increased to 450° C., noncatalytic conversion becomes significant, reaching 67.5%. When ATTM was used as a catalyst precursor, both C—C bond cleavage and hydrogenation were promoted, and NMBB conversions are over 70% in all the catalytic runs. As shown in FIG. 10, adding water to the runs with ATTM substantially enhanced the catalytic reaction: NMBB conversions increased from 78.9 to 99.3% for runs at 350° C. The promoting effect of water is still apparent for runs at 375-400° C., but the net increase in conversion becomes smaller because the NMBB conversions are already over 92% with ATTM without added water. It is clear from these results that the use of ATTM with added water is more effective than ATTM alone for NMBB conversion, particularly at lower temperatures.

Both types of catalytic runs (ATTM, and ATTM+H₂O) show similar patterns of product distributions. For the run with ATTM and ATTM+H₂O, naphthalene and 4-methylbibenzyl are the major products, indicating that both catalysts effectively promote the cleavage of aromatic-aliphatic C—C bond a in NMBB. However for noncatalytic run at 425° C. toluene and 1-(p-tolylmethyl)naphthalene, abbreviated as TMN, are the major products. This indicates that the cleavage of band d in NMBB occurs predominantly in noncatalytic runs at higher temperatures. The weakest bond in NMBB is bond d. The cleavage of the bond d in NMBB seems to occur predominantly under thermal reaction conditions over 400° C. For the run with Mo sulfide catalyst only catalyst-mediated reactions occur below 375° C., but at over 400° C. both catalytic and thermal reactions occur. Disappearance of TMN in the products at 425° C. seems to be due to secondary reaction of TMN or quick decomposition of NMBB in early stage of catalytic reaction. It is clear that the reaction pathways in catalytic and noncatalytic runs are different.

The difference in NMBB conversion between the two types of catalytic runs is large at 350° C. using 1.48 g of n-tridecane, about 20%; however the difference becomes smaller at 375-425° C. because the conversions are very high. In order to further clarify the difference in activity between the catalysts prepared from ATTM and ATTM+H₂O, NMBB reaction was conducted using larger amount of n-tridecane solvent (2.95 g). FIG. 11 summarizes the results. FIGS. 12 and 13 compare the performance of the in-situ generated catalysts for the NMBB reaction at 350° C. in the presence of 2.95 g and 1.48 g oft solvent, respectively. NMBB conversions at 350-425° C. with the catalyst in-situ generated from ATTM+H₂O are still high, ranging from 91.2 to 99.9%. These values are similar to the corresponding data in FIG. 10 with smaller amount of solvent. However, NMBB conversions with the catalyst from ATTM alone at 350-425° C. dropped significantly when n-tridecane solvent was increased from 1.48 to 2.95 g. For example, the conversions with ATTM alone decreased from 78.9 to 37.4% at 350° C., and from 92.4 to 67.6% at 375° C. These results suggest that the Mo sulfide catalysts in-situ generated from ATTM+H₂O are substantially more active than those from ATTM alone. Moreover, the Mo sulfide catalysts in-situ generated from ATTM+H₂O are highly effective for the cleavage of C—C bond a in NMBB even when its concentration is relatively low. With respect to the effect of temperature for catalyst preparation, the catalyst prepared from ATTM+H₂O at 375° C. is generally more active than those prepared at 350 and 400° C.

An issue that remains unclear from the one-step test is the role of water addition in catalytic conversion of NMBB. Does water promote the catalytic reaction, or does water addition result in highly active catalyst? To clarify the role of water and the activity of the catalyst from ATTM+H₂O, the two-step test was conducted. In the first step, the ATTM precursor was first decomposed in the presence of 2.95 g of n-tridecane with added water under H₂ pressure at 350, 375 and 400° C., respectively. In the second step, the water vapor and the NH₃ and H₂S gases generated from ATTM decomposition under H₂ pressure were removed from the reactor by hot venting at 200° C., and then NMBB was charged into the reactor and reaction was conducted at 350° C. for 30 min.

FIG. 14 shows the result of two-step tests of NMBB. The conversions of NMBB from the two-step tests are considerably higher than those of one-step tests at 350° C. As can he seen from comparison of FIG. 14 with FIG. 10, the conversion increased from 93.1% in the one-step tests to 99% in the two-step test. After the removal of water, the catalyst became more active. In the work on dinaphthyl ether (DNE), it was found that the catalysts generated from ATTM+H₂O in the one-step tests are highly active for C—O bond cleavage. The two-step tests indicated that added water is effective for generating highly active catalyst, but when the active catalyst has been generated, the H₂O addition itself has an inhibiting effect on catalytic conversion of DNE. In other words, water itself does not promote catalytic or noncatalytic conversion of DNE. These results indicate that water addition is effective for generation of active Mo sulfide from ATTM; but when the active catalyst has been generated, the water has an inhibiting effect on the C—O bond cleavage or hydrogenation of aromatic ring in DNE reaction.

In addition, as mentioned above the catalyst prepared from ATTM+H₂O at 375° C. is generally more active than those prepared at 350 and 400° C. in the onestep tests. In the two-step tests, NMBB conversions with all the catalysts prepared at 350, 375 and 400° C. are almost 100%. However, the yield of the major hydrogenation product, tetralin, is the highest with the catalyst generated from ATTM+H₂O at 375° C., as shown in FIG. 14.

The chemical analysis of the catalysts from ATTM alone and ATTM+H₂O gives S-to-Mo atomic ratios of 2.03-2.04, identical to that of the commercially available MoS₂ reagent. Therefore, the Mo sulfide samples from both ATTM and ATTM+H₂O have very similar chemical composition, but differ in morphology such as particle shape (SEM), surface area (BET) and degree of layer stacking ot MoS2 slab (XRD).

Mo sulfide catalysts generated from ATTM in the presence of n-tridecane solvent with added H₂O under H₂ pressure at 350-400° C. are much more active than those from ATTM alone for cleavage of C—C bond a and hydrogenation of naphthalene ring in NMBB. Addition of water to ATTM can more than double the conversion of NMBB in the presence of a larger amount of n-tridecane solvent at 350° C. Water addition is effective for generation of highly active catalyst, but water itself does not promote catalytic conversion of NMBB. Removal of water after ATTM decomposition at 350-400° C. under H2 pressure gives a highly active Mo sulfide catalyst.

The following are ranges and additives that can enhance the method of the present invention described above. The organic solvent can include the use of a normal alkane, hydrocarbons, petroleum products or distillate fractions of petroleum. The hydrocarbons used as the organic solvent can be a mixture of alkanes and aromatic compounds. The petroleum products or distillate fractions of petroleum used as the organic solvent preferably have a boiling point within the range of 60° C. and 460° C. The decomposing of the ammonium tetrathiomolybdate in the organic solvent with added water under H₂ pressure can be performed under heat in a reactor and then the reactor and its contents can be quickly cooled. The H₂ pressure during the process can be from 15 psi to 1500 psi, where psi is pounds per square inch. The heating during decomposition can be in the range between 300° C. and 550° C. The weight ratio of the water to the ammonium tetrathiomolybdate is preferably in the range of 0.05 to 150. The decomposition of ammonium tetrathiomolybdate can also be performed in a continuous flow reactor in a temperature range of 300° C. and 550° C. while under pressure in the range of 15 psi to 1000 psi. Finally, the decomposition can be performed in the presence of nickel or cobalt compounds. Examples of such compounds are Ni(NO₃)₂, (CH₃CO₂)Ni, Co(NO₃)₂ or (CH₃CO₂)Co.

While different embodiments of the invention have been described in detail herein, it will be appreciated by those skilled in the art that various modifications and alternatives to the embodiments could be developed in light of the overall teachings of the disclosure. Accordingly, the particular arrangements are illustrative only and are not limiting as to the scope of the invention that is to be given the full breadth of any and all equivalents thereof. 

We claim:
 1. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said organic solvent is a normal alkane.
 2. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said decomposing is performed in a reactor under H₂ pressure in the range of 15 psi to 1500 psi.
 3. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said decomposing is performed at a temperature range between 300° C. and 550° C.
 4. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said organic solvent is a hydrocarbon.
 5. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said organic solvent is a hydrocarbon mixture of alkanes and aromatic compounds.
 6. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said organic solvent is a distillate fraction of petroleum.
 7. The method of claim 6, wherein said distillate fraction of petroleum has a boiling point in the range of 60° C. and 460° C.
 8. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said organic solvent is a petroleum product.
 9. The method of claim 8, wherein said petroleum product has a boiling point in the range of 60° C. and 460° C.
 10. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein weight ratio of said water to said ammonium tetrathiomolybdate is preferably in the range of 0.05 to
 150. 11. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said H₂ pressure in the range of 15 psi to 1500 psi.
 12. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said decomposition of ammonium tetrathiomolybdate is performed in a continuous flow reactor in a temperature range of 300° C. and 550° C., while under pressure in the range of 15 psi to 1000 psi.
 13. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said decomposing is performed in the presence of an added compound containing nickel.
 14. The method of claim 13, wherein said added compound containing nickel is Ni(NO₃)₂.
 15. The method of claim 13, wherein said added compound containing nickel is (CH₃CO₂)Ni.
 16. A method of preparing a Mo Sulfide catalyst comprising decomposing ammonium tetrathiomolybdate in an organic solvent with added water under H₂ pressure in a reactor, wherein the decomposing of the ammonium tetrathiomolybdate is preformed under heat, wherein said decomposing is performed in the presence of an added compound containing colbalt.
 17. The method of claim 16, wherein said added compound containing cobalt is Co(NO₃)₂.
 18. The method of claim 16, wherein said added compound containing cobalt is (CH₃CO₂)Co. 